MEDICAL ANTISTATIC POLYETHYLENE FILM

Optimum Plastics engineered and manufactures this film for a client in the medical industry. The matte embossed film has antistatic and non-glare properties that are necessary for its application as a medical drape. The film is produced from polyethylene resins and an antistatic additive; the double-sided (MH) matte emboss creates the non-glare feature.

This film is manufactured in various widths (1.5″ to 84″) and thicknesses (1.5 mil – 30 mil); material is wound as a single wound sheet on a roll with up to a 22″ OD.

The matte embossed polyethylene film is extensively tested and analyzed by QC to ensure adherence to the customer’s specifications and our highest standards for quality. Various quality tests are available per customer request outside of our standard testing.

Highlights of the Non-Glare Antistatic Polyethylene Film Product

Product Description
This film is used as a medical drape and provides antistatic and non-glare properties.
Cast Extrusion Capabilities
Matte Embossed Polyethylene film
Equipment Used to Manufacture Part
Cast Extrusion Lines
Overall Part Dimensions
Width: 1.5″ – 84″
Thickness: 1.5 mil – 30 mil O.D.: up to 22″ outside diameter
Length: Varies to meet customer specification
Material Finish
Matte Emboss Pattern
In process testing/inspection performed
Lab Analysis
Tear testing per ASTM D1922
Tensile/elongation testing per ASTM D882
Secant modulus testing per ASTM D882
DSC melt testing per ASTM D3418
Coefficient of Friction – Static and Kinetic per ASTM D1894
Surface roughness
Emboss thickness per ASTM D374
Gloss (60degrees) per ASTM D2457
Corona treat, surface dyne level per ASTM D5946
Opacity testing
Color matching

Volume
Minimum Order Quantity 500 lbs
Delivery/Turnaround Time
3 Weeks + shipping
Packaging
3 inch or 6 inch Core
Rolls are Stretched Wrapped on a Pallet unless Otherwise Specified
Delivery Location
Worldwide
Standards Met
All materials are produced to customer specifications after receipt of order
Product Name
MH100C3 Matte Embossed Poly with Antistat